作者：MOTOKI HAYASHI;EIJI HOSOI;KATSUHIKO MAEDA;
作者單位：
刊名：Taikabutsu Overseas
ISSN：0285-0028
出版年：2001-01-05
卷：21
期：3
起頁(yè)：202
止頁(yè)：0
分類號(hào)：TQ175
語(yǔ)種：英文
關(guān)鍵詞：
內(nèi)容簡(jiǎn)介Alumina-magnesia castables have become a principal material for unshaped refractories for steel ladle linings. A feature of this castable is densification through spinel formation at high temperature, resulting in prevention of slag penetration and superior resistance against slag corrosion. However, as a disadvantage, failure by peeling and wearing takes place in some operational conditions, making a difficult compromise. In the present paper, a study was made on the change of corrosion resistance with differences in slag compositions.