作者：ZHANG Tao,WEI Yaowu,YU Hui,HAN Bingqiang,LI Nan
作者單位：The State Key Laboratory of Refractories and Metallurgy,Wuhan University of Science and Technology
刊名：China’s Refractories
ISSN：1004-4493
出版年：2017-03-15
卷：26
期：1
起頁：18-23
止頁：
分類號：TQ175.1
語種：英文
關鍵詞：
內容簡介Active lime was used to produce Ca(OH)2fine powder.And then Ca(OH)2fine powder with analytically pure CeO2fine powder(0,0.2%,0.4%,0.6%,0.8%and1.0%by mass,respectively)were mixed via wet mixing.After drying and ball milling,the specimens were pressed and fired at 1 450℃,1 500℃,1 550℃,1 600℃and1 650℃,respectively.The hydration resistance of the specimens was evaluated by measuring the mass gain after soaking the specimens in a chamber kept at 20℃and90%relative humidity.The influences of CeO2and calcination temperature on the hydration resistance of CaO aggregates were investigated by determination of bulk density,apparent porosity,and XRD,SEM and EDS analysis.The results show that:(1)the sintering of CaO aggregates is promoted by CeO2addition and the hydration resistance of CaO aggregates is improved;(2)CeO2mainly locates in CaO grain boundary,some CeO2is solved in the CaO grains which improves CaO sintering;(3)the appropriate calcination temperature is 1 550℃.When the calcination temperature is below 1 550℃,the specimens are sintered inadequately.The density and hydration resistance of CaO aggregates are nearly stable when the calcination temperature is above 1 550℃.
所需耐材幣：0