作者：GENG Qiankun,TIAN Xuekun,WANG Hongsen,SHEN Jiaxin,OUYANG Deze,ZHAO Fei,LIU Xinhong
作者單位：Henan Key Laboratory of High Temperature Functional Ceramics, School of Material Science and Engineering, Zhengzhou University
刊名：China's Refractories
ISSN：1004-4493
出版年：2024-03-15
卷：33
期：1
起頁：34-39
止頁：
分類號：TQ175.712.1
語種：英文
關鍵詞：
內容簡介To broaden the application of SiO2 sol-bonded castables, using micro-or nano-Al2O3 powder and SiO2 gel powder as the main raw materials, the effects of CaO impurity on the formation of mullite by the reaction of Al2O3 and SiO2 at different temperatures（1 350, 1 400, 1 500, and 1 600 ℃） in different atmospheres（oxidation atmosphere and reduction atmosphere） were studied. The results show that in the oxidizing atmosphere, the introduction of CaO can promote the formation of mullite. When the temperature increases from 1 350 ℃ to 1 600 ℃, the amount of mullite formed gradually increases. In the reducing atmosphere, the introduction of CaO is not conducive to the formation of mullite, and the amount of mullite decreases with the increasing temperature. The smaller the particle size of Al2O3, the more easily it reacts with SiO2 gel powder to form mullite.
所需耐材幣：0